PC50 Super-gloss Epoxy Coating

PC50 is a specially formulated 2-component epoxy coating that delivers a durable and high gloss surface.

Purpose of use:

Designed for a durable surface finish, suitable for brush or roller application, used in conjunction with a primer and base, suitable for interior surfaces. This paint delivers a high-gloss surface finish, which is suitable for metal and non-metallic surfaces, providing a variety of color coatings to the surface.

Performance

• Excellent adhesion.
• Ease of construction.
• Quick drying, long shelf life.
• High permeability.

• Volume Solids: 50%
• Coverage: 10 m2/L (DFT 50 microns)
• Type: Two-component
• Packing Ratio: 4L Base (Part A) : 1L Hardener (Part B)
• Color Availability: Variety
• Flash Point: 30oC
• Thinner: AT-02

PRACTICAL APPLICATION RATES – microns per coa

AVERAGE DRYING TIME

SURFACE PREPARATION

Steel: Abrasive blast clean to a minimum standard of Sa2.5 (ISO8501-1:1988) or SSPCSP10. An average surface profile of 50-75 microns is required. The surface to be coated must be clean and dry and free from all visible traces of surface contaminants. Manually prepared surfaces should be prepared to a minimum standard of St3 (ISO8501-1:1988) at the time of coating.

APPLICATION DATA

• Application methods: Brush/ Roller, Airless Spray, and Conventional Spray.
• Mixing ratio (by volume): 4 parts Base to 1 part Hardener.
• Thinner: Thinner AT02 (Maximum 5% addition).
• Airless Spray: Nozzle Size: 0.46mm (18 thou) Fan Angle: 65°. Operating Pressure: 155kg/cm² (2200 psi).
• Conventional Spray: Nozzle Size: 1.27mm (50 thou). Atomising Pressure: 2.8 kg/cm² (40 psi). Fluid Pressure: 0.4 kg/cm² (6 psi).
• Brush/Roller: This product is suitable for brush application. Application of more than one coat may be necessary to give equivalent dry film thickness to a single spray-applied coat.

APPLICATION CONDITIONS AND OVERCOATING

This product should preferably be applied at a temperature in excess of 10°C. In conditions of high relative humidity i.e. 80-85%, good ventilation conditions are essential. The substrate temperature should be at least 3°C above the dew point. At application temperature below 10°C, drying and curing time will be significantly impaired. Application at a temperature below 5°C is not recommended. In order to achieve optimum water and chemical resistance, the temperature needs to be maintained above 10°C during curing.

Consult Safety Data Sheet for information on the safe handling and application of this product.